- 吸水率 [%]: 4.5
- 弯曲强度 [MPa]: 5.62
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 4.5 % @Time 7200 sec | 4.5 % @Time 2.00 hour | boil; cured 2 hours @ 93°C | ||
| Viscosity | 2300 cP | 2300 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 46 @Temperature 75.0 °C | 46 @Temperature 167 °F | cured 2 hrs. @ 93°C | ||
| 79 @Temperature 25.0 °C | 79 @Temperature 77.0 °F | cured 2 hrs. @ 93°C | |||
| 86 @Temperature 0.000 °C | 86 @Temperature 32.0 °F | cured 2 hrs. @ 93°C | |||
| 87 @Temperature -60.0 °C | 87 @Temperature -76.0 °F | cured 2 hrs. @ 93°C | |||
| Tensile Strength, Ultimate | 5.62 MPa | 815 psi | cured 2 hours @ 93°C | ||
| 27.41 MPa | 3975 psi | cured 8 hours @ 93°C | |||
| Elongation at Break | 23 % | 23 % | cured 8 hours @ 93°C | ||
| 76 % | 76 % | cured 2 hours @ 93°C | |||
| Shear Strength | 9.38 MPa @Temperature 75.0 °C | 1360 psi @Temperature 167 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | ||
| 24.5 MPa @Temperature 25.0 °C | 3560 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| 36.9 MPa @Temperature 0.000 °C | 5350 psi @Temperature 32.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 6.60e+7 ohm-cm @Temperature 150 °C | 6.60e+7 ohm-cm @Temperature 302 °F | cured 2 hours @ 93°C | ||
| 2.50e+8 ohm-cm @Temperature 112 °C | 2.50e+8 ohm-cm @Temperature 234 °F | cured 2 hours @ 93°C | |||
| 2.90e+8 ohm-cm @Temperature 100 °C | 2.90e+8 ohm-cm @Temperature 212 °F | cured 2 hours @ 93°C | |||
| 8.20e+12 ohm-cm @Temperature 25.0 °C | 8.20e+12 ohm-cm @Temperature 77.0 °F | cured 2 hours @ 93°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 30 min @Temperature 25.0 °C | 30 min @Temperature 77.0 °F | 200 g | ||
| Gel Time | 11.0 min @Temperature 93.0 °C | 11.0 min @Temperature 199 °F | 10 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 100 | AboCast 8110-7 | |||
| 8 | AboCure 8110-1 | ||||