- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.25
- 断裂伸长率 [%]: 131
- 弯曲强度 [MPa]: 62.05
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in³ | |
| Water Absorption | 0.25 - 0.30 % | 0.25 - 0.30 % | (60x10X4 mm bar) after 10 days at 20°C (77°F) |
| 0.30 - 0.35 % | 0.30 - 0.35 % | (60x10X4 mm bar) after 1 hour at 100°C (212°F) | |
| Viscosity | 5000 - 50000 cP @Temperature 120 °C | 5000 - 50000 cP @Temperature 248 °F | |
| Vapor Pressure | <= 0.0000133 bar | <= 0.0100 torr | AboCure, at 20°C |
| <= 0.00133 bar | <= 1.00 torr | AboCast, at 180°C | |
| 0.00133 bar | 1.00 torr | AboCure, at 100°C | |
| 0.00373 bar | 2.80 torr | AboCure, at 120°C | |
| 0.0133 bar | 10.0 torr | AboCure, at 135°C | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 62.05 MPa | 9000 psi | |
| Flexural Yield Strength | 131 MPa | 19000 psi | |
| Compressive Yield Strength | 193.1 MPa | 28010 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.50e+16 ohm-cm | >= 1.50e+16 ohm-cm | |
| Dielectric Constant | 3.7 - 4.0 @Frequency 50 Hz | 3.7 - 4.0 @Frequency 50 Hz | |
| 3.9 - 4.2 @Frequency 1000 Hz | 3.9 - 4.2 @Frequency 1000 Hz | ||
| 4.0 - 4.2 @Frequency 1e+6 Hz | 4.0 - 4.2 @Frequency 1e+6 Hz | ||
| Dielectric Strength | 17.72 - 20.67 kV/mm @Thickness 3.17 mm | 450.1 - 525.0 kV/in @Thickness 0.125 in | Short time value |
| Dissipation Factor | 0.0090 - 0.014 @Frequency 50 Hz | 0.0090 - 0.014 @Frequency 50 Hz | |
| 0.0090 - 0.015 @Frequency 1000 Hz | 0.0090 - 0.015 @Frequency 1000 Hz | ||
| 0.015 - 0.025 @Frequency 1e+6 Hz | 0.015 - 0.025 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 - 35.0 µm/m-°C @Temperature 20.0 °C | 16.7 - 19.4 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.590 - 0.670 W/m-K | 4.09 - 4.65 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Deflection temperature; load unknown |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 130 - 140 °C | 266 - 284 °F | |
| Pot Life | 90 min | 90 min | at 120°C (250°F) |