- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.6
- 断裂伸长率 [%]: 89.63
- 弯曲强度 [MPa]: 62.05
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | |
| Water Absorption | 0.60 - 0.70 % | 0.60 - 0.70 % | (60x10X4 mm bar) after 10 days at 20°C (77°F) |
| 1.0 - 1.1 % | 1.0 - 1.1 % | (60x10X4 mm bar) after 1 hour at 100°C (212°F) | |
| Viscosity | 2000 - 2600 cP | 2000 - 2600 cP | |
| Vapor Pressure | <= 0.0000133 bar | <= 0.0100 torr | AboCure, at 20°C |
| <= 0.00133 bar | <= 1.00 torr | AboCast, at 100°C | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 62.05 MPa | 9000 psi | |
| Modulus of Elasticity | 3.102 GPa | 449.9 ksi | |
| Flexural Yield Strength | 89.63 MPa | 13000 psi | |
| Compressive Yield Strength | 82.74 MPa | 12000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.50e+16 ohm-cm | >= 1.50e+16 ohm-cm | |
| Dielectric Constant | 3.6 - 3.9 @Frequency 1e+6 Hz | 3.6 - 3.9 @Frequency 1e+6 Hz | |
| 4.0 - 4.1 @Frequency 50 Hz | 4.0 - 4.1 @Frequency 50 Hz | ||
| Dissipation Factor | 0.010 - 0.020 | 0.010 - 0.020 | |
| 0.015 - 0.025 @Frequency 1e+6 Hz | 0.015 - 0.025 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 95.0 - 100 µm/m-°C @Temperature 20.0 °C | 52.8 - 55.6 µin/in-°F @Temperature 68.0 °F | |
| Maximum Service Temperature, Air | 55.0 °C | 131 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Pot Life | 150 min | 150 min | at 20°C (68°F), 30 min/40°C (105°F), 15 min/60°C (140°F) |