- 吸水率 [%]: 0.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 0.10 - 0.50 % | 0.10 - 0.50 % | 24-200 hours |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | >= 85 | >= 85 | |
| Tensile Strength at Break | 35.9 MPa | 5200 psi | |
| Elongation at Break | 3.6 % | 3.6 % | |
| Flexural Strength | 49.6 MPa | 7200 psi | |
| Compressive Strength | 86.2 MPa | 12500 psi | |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.586 - 0.669 W/m-K | 4.06 - 4.64 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 65.0 - 70.0 °C | 149 - 158 °F | Deflection temperature after room temperature cure |
| 93.0 °C | 199 °F | Deflection temperature after post-cure | |
| Processing Properties | Metric | English | Comments |
| Pot Life | 120 - 180 min | 120 - 180 min | 1-2 lbs at 25°C |