- 吸水率 [%]: 0.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 0.10 - 0.50 % | 0.10 - 0.50 % | 24-200 hours |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | >= 90 | >= 90 | |
| Tensile Strength at Break | 57.9 MPa | 8400 psi | |
| Elongation at Break | 1.0 % | 1.0 % | |
| Flexural Strength | 73.8 MPa | 10700 psi | |
| Compressive Strength | 194 MPa | 28200 psi | |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.586 - 0.669 W/m-K | 4.06 - 4.64 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 120 - 130 °C | 248 - 266 °F | Deflection temperature after room temperature cure |
| 150 - 160 °C | 302 - 320 °F | Deflection temperature after post-cure | |
| Processing Properties | Metric | English | Comments |
| Pot Life | 300 - 480 min | 300 - 480 min | 1-2 lbs at 25°C |