| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.95 g/cc | 1.95 g/cc | |||
| Viscosity | 3000 cP | 3000 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 92 | 92 | |||
| Flexural Strength | 84.8 MPa | 12300 psi | ASTM D790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |||
| Dielectric Constant | 4.7 @Frequency 1000 Hz | 4.7 @Frequency 1000 Hz | |||
| Dielectric Strength | 18.9 kV/mm | 480 kV/in | |||
| Dissipation Factor | 0.010 | 0.010 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 34.0 µm/m-°C @Temperature 20.0 °C | 18.9 µin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 1.21 W/m-K | 8.40 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 185 °C | 365 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Shrinkage | 0.30 % | 0.30 % | Cure Shrinkage | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 min | 4.00 hour | 2 hrs at 160°F; 2 hrs at 300°F (Recommended Cure) | ||
| 360 min | 6.00 hour | at 250°F (Alternate Cure) | |||
| Pot Life | >= 480 min | >= 480 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Excellent | ||||
| Mix Ratio by Weight | 100:25 | resin:hardener | |||