| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 89 | 89 | |||
| Flexural Strength | 97.2 MPa | 14100 psi | ASTM D790 | ||
| Shear Strength | 17.9 MPa | 2600 psi | ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | |||
| Dielectric Constant | 6.5 @Frequency 1000 Hz | 6.5 @Frequency 1000 Hz | |||
| Dielectric Strength | 16.5 kV/mm | 420 kV/in | |||
| Dissipation Factor | 0.090 | 0.090 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 27.0 µm/m-°C @Temperature 20.0 °C | 15.0 µin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 1.59 W/m-K | 11.0 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Shrinkage | 0.50 % | 0.50 % | Cure Shrinkage | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min | 2.00 hour | at 200°F (Alternate Cure) | ||
| 1440 - 2880 min | 24.0 - 48.0 hour | Room Temperature (Recommended Cure) | |||
| Pot Life | 60 min | 60 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Good | ||||
| Mix Ratio by Weight | 100:11 | resin:hardener | |||