- 密度 [g/cm3]: 1.82
- 弯曲强度 [MPa]: 62.0
- 弯曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in³ | |
| Viscosity | 8500 cP @Temperature 175 °C | 8500 cP @Temperature 347 °F | Automatic orifice Viscosity |
| Linear Mold Shrinkage | 0.0037 cm/cm | 0.0037 in/in | |
| Spiral Flow | 80.0 - 110 cm | 31.5 - 43.3 in | 177°C/1000 psi |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 73 | 73 | |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | |
| Flexural Strength | 110 MPa | 16000 psi | |
| Flexural Modulus | 13.0 GPa | 1890 ksi | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.68 @Frequency 1000 Hz | 3.68 @Frequency 1000 Hz | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz | 0.0020 @Frequency 1000 Hz | |
| Arc Resistance | 180 sec | 180 sec | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.5 µm/m-°C @Temperature 20.0 °C | 10.3 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | 165 °C | 329 °F | |
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 185 °C | 338 - 365 °F | Molding temperature |