- 密度 [g/cm3]: 1.86
- 弯曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.86 g/cc | 0.0672 lb/in³ | |
| Viscosity | 16500 cP @Temperature 175 °C | 16500 cP @Temperature 347 °F | Automatic orifice Viscosity |
| Spiral Flow | 63.0 - 87.0 cm | 24.8 - 34.3 in | 177°C/1000 psi |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 81 | 81 | |
| Flexural Strength | 131 MPa | 19000 psi | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.8 @Frequency 1000 Hz | 3.8 @Frequency 1000 Hz | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz | 0.0020 @Frequency 1000 Hz | |
| Arc Resistance | 180 sec | 180 sec | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C | 10.0 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 56.0 µm/m-°C @Temperature 20.0 °C | 31.1 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | 153 °C | 307 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 185 °C | 338 - 365 °F | Molding temperature |