- 密度 [g/cm3]: 1.8
- 弯曲模量 [MPa]: 15.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | |
| Viscosity | 11000 cP @Temperature 175 °C | 11000 cP @Temperature 347 °F | Automatic orifice Viscosity |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Spiral Flow | 72.0 cm | 28.3 in | 165°C/1000 psi |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 80 | 80 | |
| Flexural Strength | 124 MPa | 18000 psi | |
| Flexural Modulus | 15.0 GPa | 2180 ksi | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.5 @Frequency 1000 Hz | 3.5 @Frequency 1000 Hz | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | |
| Dissipation Factor | 0.0030 @Frequency 1000 Hz | 0.0030 @Frequency 1000 Hz | |
| Arc Resistance | 180 sec | 180 sec | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 21.0 µm/m-°C @Temperature 20.0 °C | 11.7 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature 20.0 °C | 37.2 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | 157 °C | 315 °F | |
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 165 - 175 °C | 329 - 347 °F | Molding temperature |