- 密度 [g/cm3]: 1.9
- 弯曲强度 [MPa]: 68.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | |
| Viscosity | 30000 cP | 30000 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 80 | 80 | |
| Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | |
| Elongation at Break | 1.2 % | 1.2 % | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+8 ohm-cm | 1.00e+8 ohm-cm | |
| Dielectric Strength | 3.94 kV/mm | 100 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 5.04 W/m-K | 35.0 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| Shrinkage | 0.10 % | 0.10 % | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 60.0 min | 1.00 hour | at 250°F |