- 密度 [g/cm3]: 1.1
- 弯曲强度 [MPa]: 71.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Viscosity | 600 cP | 600 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 80 | 80 | |
| Tensile Strength, Ultimate | 71.0 MPa | 10300 psi | |
| Elongation at Break | 5.0 % | 5.0 % | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 64.0 µm/m-°C @Temperature 20.0 °C | 35.6 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.576 W/m-K | 4.00 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 316 °C | 600 °F | |
| Shrinkage | 0.50 % | 0.50 % | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 240 min | 4.00 hour | at 250°F |