- 密度 [g/cm3]: 1.15
- 弯曲强度 [MPa]: 32.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.21 g/cc | 0.0415 - 0.0437 lb/in³ | |
| Solids Content | >= 99 % | >= 99 % | |
| Viscosity | 500000 cP @Shear Rate 1.00 1/s, Temperature 40.0 °C | 500000 cP @Shear Rate 1.00 1/s, Temperature 104 °F | cone/plate |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 32.0 MPa | 4640 psi | ISO 527-1 |
| Elongation at Break | 15 % | 15 % | ISO 527-1 |
| Modulus of Elasticity | 1.60 GPa | 232 ksi | ISO 527-1 |
| Adhesive Bond Strength | 30.0 MPa @Thickness 2.00 mm | 4350 psi @Thickness 0.0787 in | Lap Shear (25 x 10 x 0.2 mm) (CRS St 1203, 170°C/30); EN 1465 |
| Peel Strength | 4.00 kN/m | 22.8 pli | T-Peel (CRS St 1203, 0.5mm) |
| 28.0 kN/m | 160 pli | Impact Peel | |
| Thermal Properties | Metric | English | Comments |
| Flash Point | >= 150 °C | >= 302 °F | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min | 0.500 hour | 170°C |
| 60.0 min | 1.00 hour | 155°C | |