| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 25.0 °C | 77.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 46.0 MPa | 6670 psi | |||
| Elongation at Break | 1.7 % | 1.7 % | |||
| Tensile Modulus | 4.25 GPa | 616 ksi | |||
| Compressive Strength | 158.6 MPa | 23000 psi | |||
| Adhesive Bond Strength | 20.0 MPa @Temperature 93.0 °C | 2900 psi @Temperature 199 °F | Tensile Lap Shear | ||
| 22.8 MPa @Temperature -55.0 °C | 3310 psi @Temperature -67.0 °F | Tensile Lap Shear | |||
| 29.0 MPa @Temperature 25.0 °C | 4210 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Peel Strength | 3.60 kN/m | 20.5 pli | Bell Peel | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 177 °C | 351 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 66.0 °C | 1.00 hour @Temperature 151 °F | |||
| 7200 - 10100 min @Temperature 25.0 °C | 120 - 168 hour @Temperature 77.0 °F | ||||
| Pot Life | 100 min | 100 min | |||
| Descriptive Properties | |||||
| Consistency | Thixotropic | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:17 | ||||
| Peel Strength | Low | ||||