| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 25.0 °C | 77.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 55.7 MPa | 8080 psi | |||
| Elongation at Break | 2.6 % | 2.6 % | |||
| Tensile Modulus | 4.90 GPa | 711 ksi | |||
| Compressive Strength | 96.6 MPa | 14000 psi | |||
| Compressive Modulus | 2.95 GPa | 428 ksi | |||
| Adhesive Bond Strength | 15.9 MPa @Temperature -55.0 °C | 2310 psi @Temperature -67.0 °F | Tensile Lap Shear | ||
| 16.6 MPa @Temperature 93.0 °C | 2410 psi @Temperature 199 °F | Tensile Lap Shear | |||
| 27.6 MPa @Temperature 25.0 °C | 4000 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Peel Strength | 2.80 kN/m | 16.0 pli | Bell Peel | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 177 °C | 351 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 66.0 °C | 1.00 hour @Temperature 151 °F | |||
| 7200 - 10100 min @Temperature 25.0 °C | 120 - 168 hour @Temperature 77.0 °F | ||||
| Pot Life | 100 min | 100 min | |||
| Descriptive Properties | |||||
| Consistency | Thixotropic | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:17 | ||||
| Peel Strength | Low | ||||