- 密度 [g/cm3]: 1.5
- 弯曲模量 [MPa]: 65.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 - 1.65 g/cc | 0.0542 - 0.0596 lb/in³ | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 900 - 1200 MPa | 131000 - 174000 psi | Longitudinal | ||
| Elongation at Break | 1.4 % | 1.4 % | Longitudinal | ||
| Tensile Modulus | 136 GPa | 19700 ksi | Longitudinal | ||
| Flexural Strength | 800 - 1000 MPa | 116000 - 145000 psi | Longitudinal | ||
| Flexural Modulus | 65.0 - 85.0 GPa | 9430 - 12300 ksi | Longitudinal | ||
| Compressive Strength | 900 - 1100 MPa | 131000 - 160000 psi | Longitudinal | ||
| Descriptive Properties | |||||
| Volume Fraction Fibers, % | 55-60 | ||||