- 弯曲强度 [MPa]: 8.89
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | silicone property; Arlon SQA-TMS-024 | ||
| Thickness | 88.9 microns | 3.50 mil | side 1; Arlon SQA-TMS-003 | ||
| 140 microns | 5.50 mil | side 2; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | substrate; Arlon SQA-TMS-003 | |||
| 432 microns | 17.0 mil | overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 62 | 62 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 8.89 MPa | 1290 psi | silicone property; ASTM D412 | ||
| Elongation at Break | 150 % | 150 % | silicone property; ASTM D412 | ||
| Adhesive Bond Strength | 0.0207 MPa | 3.00 psi | Arlon SQA-TMS-011 | ||
| Tear Strength | 14.5 kN/m | 83.0 pli | Die B; silicone property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 31.9 kV/mm | 811 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | V-1 | V-1 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | |||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | ||||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Gray | ||||