- 密度 [g/cm3]: 1.36
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | Side 2; Arlon SQA-TMS-024 | ||
| 1.38 g/cc | 0.0499 lb/in³ | Side 1; Arlon SQA-TMS-024 | |||
| Thickness | 63.5 microns | 2.50 mil | Interleave | ||
| 102 microns | 4.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 178 microns | 7.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 381 microns | 15.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 660 microns | 26.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 51 | 51 | Side 1; ASTM D2240 | ||
| 56 | 56 | Side 2; ASTM D2240 | |||
| Tensile Strength | 5.17 MPa | 750 psi | Side 2; ASTM D412 | ||
| 5.31 MPa | 770 psi | Side 1; ASTM D412 | |||
| Elongation at Break | 265 % | 265 % | Side 2; ASTM D412 | ||
| 330 % | 330 % | Side 1; ASTM D412 | |||
| Tear Strength | 10.5 kN/m | 60.0 pli | Side 2; ASTM D624 | ||
| 10.9 kN/m | 62.0 pli | Side 1; ASTM D624 | |||
| Peel Strength | 1.45 kN/m | 8.30 pli | Bond Strength; Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 16.1 kV/mm | 410 kV/in | Arlon SQA-TMS-020 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Total Product Weight (oz/yd2) | 29.3 | Arlon SQA-TMS-025 | |||