| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene Interleave | ||
| 76.2 - 102 microns | 3.00 - 4.00 mil | Side 1 | |||
| 76.2 - 102 microns | 3.00 - 4.00 mil | Side 2 | |||
| 102 microns | 4.00 mil | Prime Coated 112 Fiberglass, Substrate | |||
| 279 - 330 microns | 11.0 - 13.0 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 45 - 55 | 45 - 55 | Compound Property | ||
| Tensile Strength | >= 5.86 MPa | >= 850 psi | Compound Property | ||
| Elongation at Break | >= 350 % | >= 350 % | Compound Property | ||
| Peel Strength | >= 1.40 kN/m | >= 8.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | <= 3.0 | <= 3.0 | [in], Char Length | ||
| <= 25 | <= 25 | [sec], Flame and Glow Time; FTMS 191A, Method 5903 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 10.3 - 12.3 | ||||
| Uncoated Fabric Break Strength | 80 lb/in | Fill Direction, Substrate Property | |||
| 90 lb/in | Warp Direction, Substrate Property | ||||