- 密度 [g/cm3]: 1.18
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 25.4 microns | 1.00 mil | Side 1; Arlon SQA-TMS-003 | ||
| 25.4 microns | 1.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 152 microns | 6.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 8.96 MPa | 1300 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 700 % | 700 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 43.8 kN/m | 250 pli | Die B, Silicone Property; ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| Shelf Life | 12.0 Month @Temperature 23.9 °C | 12.0 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Carmel Brown | Substrate | |||
| Translucent | Silicone | ||||
| Total Product Weight (oz/yd2) | 1.6 | Arlon SQA-TMS-025 | |||
| Uncoated Fabric Break Strength | 40 lb/in | Warp Strength, Arlon SQA-TMS-026 | |||
| 43 lb/in | Fill Strength, Arlon SQA-TMS-026 | ||||