- 密度 [g/cm3]: 1.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | Side 1 Silicone Property; Arlon SQA-TMS-024 | ||
| 1.35 g/cc | 0.0488 lb/in³ | Side 2 Silicone Property; Arlon SQA-TMS-024 | |||
| Thickness | 50.8 microns | 2.00 mil | Side 1; Arlon SQA-TMS-003 | ||
| 178 microns | 7.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 406 microns | 16.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 635 microns | 25.0 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | Side 1 Silicone Property; ASTM D2240 | ||
| 60 | 60 | Side 2 Silicone Property; ASTM D2240 | |||
| Tensile Strength | 6.21 MPa | 900 psi | Side 1 Silicone Property; ASTM D412 | ||
| 6.21 MPa | 900 psi | Side 2 Silicone Property; ASTM D412 | |||
| Elongation at Break | 200 % | 200 % | Side 1 Silicone Property; ASTM D412 | ||
| 300 % | 300 % | Side 2 Silicone Property; ASTM D412 | |||
| Peel Strength | 1.31 kN/m | 7.50 pli | Bond Strength; Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 177 °C | 0.250 hour @Temperature 350 °F | Recommended Cure Cycle; under pressure | ||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 29 | Arlon SQA-TMS-025 | |||