- 密度 [g/cm3]: 1.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Carrier | ||
| 381 microns | 15.0 mil | Product; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 88 | 88 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 4.41 MPa | 640 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 15 % | 15 % | Silicone Property; ASTM D412 | ||
| Modulus of Elasticity | 0.0483 GPa | 7.00 ksi | Arlon SQA-TMS-008 | ||
| Poissons Ratio | 0.50 | 0.50 | |||
| Shear Modulus | <= 0.000483 GPa | <= 0.0700 ksi | Arlon SQA-TMS-018 | ||
| Shear Strength | 2.41 MPa | 350 psi | Lap; ASTM D1002 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | IPC TM 650 - 2.5.5.3 | ||
| Dielectric Strength | 39.4 kV/mm | 1000 kV/in | ASTM D149 | ||
| Dissipation Factor | 0.0015 @Frequency 1.00e+6 Hz | 0.0015 @Frequency 1.00e+6 Hz | IPC TM 650 - 2.5.5.3 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | ASTM E831 | ||
| Specific Heat Capacity | 0.760 J/g-°C | 0.182 BTU/lb-°F | E1461-01 | ||
| Thermal Conductivity | 1.20 W/m-K | 8.33 BTU-in/hr-ft²-°F | ASTM E1530 | ||
| Maximum Service Temperature, Inert | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |||
| Glass Transition Temp, Tg | -116 °C | -177 °F | ASTM E1356 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 121 °C | 0.250 hour @Temperature 250 °F | Recommended Cure Cycle; Under Pressure | ||
| Shelf Life | 6.00 Month @Temperature 7.22 °C | 6.00 Month @Temperature 45.0 °F | |||
| Descriptive Properties | |||||
| Color | White | ||||
| Thermal Resistance (°C-in2/W) | 0.5 | ASTM E1530 | |||
| Total Product Weight (oz/yd2) | 19 | Arlon SQA-TMS-025 | |||