- 密度 [g/cm3]: 0.989
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.989 g/cc | 0.0357 lb/in³ | Mixed | ||
| Viscosity | 1500 - 1800 cP | 1500 - 1800 cP | B | ||
| 1400 - 2000 cP | 1400 - 2000 cP | A | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 27.6 - 31.0 MPa | 4000 - 4500 psi | |||
| Elongation at Break | 5.0 - 10 % | 5.0 - 10 % | |||
| Tensile Modulus | 1.72 - 1.90 GPa | 250 - 275 ksi | |||
| Shear Strength | 13.8 - 17.2 MPa | 2000 - 2500 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 121 °C | 250 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Flash Point | 10.6 °C | 51.0 °F | TCC | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 30 - 35 min | 30 - 35 min | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Fixture Time | 60-65 minutes | ||||
| Mix Ratio | 2:1 | By volume | |||