- 密度 [g/cm3]: 1.74
- 吸水率 [%]: 0.035
- 缺口冲击强度: 0.156
- 断裂伸长率 [%]: 55.0
- 弯曲强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 - 2.06 g/cc | 0.0629 - 0.0744 lb/in³ | Average value: 1.83 g/cc Grade Count:8 |
| Water Absorption | 0.0350 - 0.0480 % | 0.0350 - 0.0480 % | Average value: 0.0431 % Grade Count:8 |
| Linear Mold Shrinkage | 0.00173 - 0.00420 cm/cm | 0.00173 - 0.00420 in/in | Average value: 0.00261 cm/cm Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 58.0 - 61.0 | 58.0 - 61.0 | Average value: 59.2 Grade Count:5 |
| Tensile Strength, Ultimate | 31.0 - 89.0 MPa | 4500 - 12900 psi | Average value: 43.9 MPa Grade Count:8 |
| Elongation at Break | 0.236 - 0.580 % | 0.236 - 0.580 % | Average value: 0.399 % Grade Count:8 |
| Modulus of Elasticity | 10.3 - 29.0 GPa | 1490 - 4210 ksi | Average value: 15.2 GPa Grade Count:8 |
| Flexural Yield Strength | 55.0 - 163 MPa | 7980 - 23600 psi | Average value: 76.3 MPa Grade Count:8 |
| Flexural Modulus | 10.0 - 26.0 GPa | 1450 - 3770 ksi | Average value: 13.3 GPa Grade Count:8 |
| Compressive Yield Strength | 117 - 269 MPa | 17000 - 39000 psi | Average value: 151 MPa Grade Count:8 |
| Izod Impact, Notched | 0.156 - 0.174 J/cm | 0.292 - 0.326 ft-lb/in | Average value: 0.163 J/cm Grade Count:7 |
| Charpy Impact, Notched | 0.144 - 0.260 J/cm² | 0.685 - 1.24 ft-lb/in² | Average value: 0.178 J/cm² Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 32.0 - 38.0 µm/m-°C @Temperature 40.0 - 130 °C | 17.8 - 21.1 µin/in-°F @Temperature 104 - 266 °F | Average value: 34.0 µm/m-°C Grade Count:3 |
| Thermal Conductivity | 1.22 - 1.94 W/m-K @Temperature 100 - 100 °C | 8.47 - 13.5 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F | Average value: 1.58 W/m-K Grade Count:2 |
| Maximum Service Temperature, Air | 200 - 257 °C | 392 - 495 °F | Average value: 220 °C Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 - 222 °C | 356 - 432 °F | Average value: 193 °C Grade Count:8 |
| Shrinkage | 0.0100 - 0.0860 % | 0.0100 - 0.0860 % | Average value: 0.0539 % Grade Count:8 |