- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.1
- 缺口冲击强度: 8.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 - 1.90 g/cc | 0.0614 - 0.0686 lb/in³ | Molding; IS 867-1963 |
| Water Absorption | 0.10 - 0.20 % | 0.10 - 0.20 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0015 - 0.0026 cm/cm | 0.0015 - 0.0026 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | >= 80.0 MPa | >= 11600 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | >= 120 MPa | >= 17400 psi | 2mm/min.; IS 867-1963 |
| Izod Impact, Notched | >= 8.00 J/cm | >= 15.0 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 - 1.0 ohm-cm | 1.00e+12 - 1.0 ohm-cm | IS 3396-1979 |
| Surface Resistance | 3.2e+11 - 1.0 ohm | 3.2e+11 - 1.0 ohm | IS 3396-1979 |
| Dielectric Strength | >= 8.00 kV/mm @Temperature 90.0 °C | >= 203 kV/in @Temperature 194 °F | IS 2584-1963 |
| Comparative Tracking Index | >= 150 V | >= 150 V | 2824-1975 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 1.33 - 1.83 min | 0.0222 - 0.0306 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |