- 密度 [g/cm3]: 0.0288
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0288 g/cc | 0.00104 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 0.586 MPa | >= 85.0 psi | Bare, min |
| >= 0.655 MPa | >= 95.0 psi | Stabilized, min | |
| 0.724 MPa | 105 psi | Bare, typ | |
| 0.793 MPa | 115 psi | Stabilized, typ | |
| Compressive Modulus | 0.0552 GPa | 8.00 ksi | Stabilized, typ |
| Shear Modulus | 0.0103 GPa | 1.50 ksi | Plate Shear, W Direction, typ |
| 0.0262 GPa | 3.80 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 0.276 MPa | >= 40.0 psi | Plate Shear, W Direction, min |
| 0.345 MPa | 50.0 psi | Plate Shear, W Direction, typ | |
| >= 0.517 MPa | >= 75.0 psi | Plate Shear, L Direction, min | |
| 0.621 MPa | 90.0 psi | Plate Shear, L Direction, typ | |