- 拉伸强度 [MPa]: 131.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Moisture Absorption at Equilibrium | 3.69 % @Thickness 1.57 mm | 3.69 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 131 MPa @Thickness 1.57 mm | 19000 psi @Thickness 0.0620 in | CW; ASTM D638 | ||
| 159 MPa @Thickness 1.57 mm | 23000 psi @Thickness 0.0620 in | LW; ASTM D638 | |||
| Modulus of Elasticity | 8.27 GPa @Thickness 1.57 mm | 1200 ksi @Thickness 0.0620 in | CW; ASTM D229 | ||
| 8.27 GPa @Thickness 1.57 mm | 1200 ksi @Thickness 0.0620 in | LW; ASTM D229 | |||
| Flexural Strength | 103 MPa @Thickness 1.57 mm | 15000 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 228 MPa @Thickness 1.57 mm | 33000 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Compressive Strength | 269 MPa @Thickness 12.7 mm | 39000 psi @Thickness 0.500 in | ASTM D695 | ||
| Izod Impact, Unnotched | 3.74 J/cm @Thickness 12.7 mm | 7.00 ft-lb/in @Thickness 0.500 in | CW, Cond E-48/50; ASTM D256 | ||
| 12.8 J/cm @Thickness 12.7 mm | 24.0 ft-lb/in @Thickness 0.500 in | LW, Cond E-48/50; ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 5.0 @Thickness 1.57 mm | 5.0 @Thickness 0.0620 in | Permittivity, Cond D-24/23; ASTM D150 | ||
| Dissipation Factor | 0.030 @Thickness 1.57 mm | 0.030 @Thickness 0.0620 in | Cond D-24/23; ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 21.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 11.7 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| CTE, linear, Transverse to Flow | 30.8 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 17.1 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |||
| Descriptive Properties | |||||
| Bond Strength | 2400 lb | 0.5", ASTM D229 | |||
| Color | Natural | ||||