- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.26
- 断裂伸长率 [%]: 89.8
- 弯曲强度 [MPa]: 57.4
- 弯曲模量 [MPa]: 8.44
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.740 g/cc | 0.0267 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.26 % | 0.26 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | per ATM D955. Post shrinkage is 0.26% at 72hr 120ºC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 57.4 MPa | 8330 psi | ASTM D638 |
| Elongation at Break | 0.82 % | 0.82 % | ASTM D638 |
| Tensile Modulus | 9.54 GPa | 1380 ksi | ASTM D638 |
| Flexural Yield Strength | 89.8 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 8.44 GPa | 1220 ksi | ASTM D790 |
| Compressive Yield Strength | 192.1 MPa | 27860 psi | ASTM D695 |
| Charpy Impact, Notched | 0.170 J/cm² | 0.809 ft-lb/in² | ASTM D256 |
| Impact | 94 | 94 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.12e+11 ohm-cm | 2.12e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.2 @Frequency 1e+6 Hz | 5.2 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 7.40 kV/mm | 188 kV/in | Step by Step; ASTM D149 |
| 10.9 kV/mm | 277 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.066 @Frequency 1e+6 Hz | 0.066 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 160 sec | 160 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 201 °C | 394 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.47 mm | V-1 @Thickness 0.0579 in | |