- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.26
- 断裂伸长率 [%]: 82.7
- 弯曲强度 [MPa]: 60.5
- 弯曲模量 [MPa]: 9.37
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.720 g/cc | 0.0260 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.26 % | 0.26 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0033 cm/cm | 0.0033 in/in | per ATM D955. Post shrinkage is 0.13% at 72hr 120ºC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 87 | 87 | ASTM D785 |
| Tensile Strength, Ultimate | 60.5 MPa | 8770 psi | ASTM D638 |
| Elongation at Break | 0.74 % | 0.74 % | ASTM D638 |
| Tensile Modulus | 9.87 GPa | 1430 ksi | ASTM D638 |
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 9.37 GPa | 1360 ksi | ASTM D790 |
| Compressive Yield Strength | 207 MPa | 30000 psi | ASTM D695 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ASTM D256 |
| Impact | 95 | 95 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.6811e+12 ohm-cm | 2.6811e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.8 @Frequency 1e+6 Hz | 4.8 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 14.7 kV/mm | 373 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.037 @Frequency 1e+6 Hz | 0.037 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 170 sec | 170 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 205 °C | 401 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.47 mm | V-1 @Thickness 0.0579 in | |