- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.267
- 缺口冲击强度: 0.155
- 弯曲强度 [MPa]: 57.0
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.710 g/cc | 0.0257 lb/in³ | ASTM D1895 |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Water Absorption | 0.267 % | 0.267 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0083 cm/cm | 0.0083 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 79 | 79 | ASTM D785 |
| Tensile Strength, Ultimate | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 0.78 % | 0.78 % | ASTM D638 |
| Tensile Modulus | 9.10 GPa | 1320 ksi | ASTM D638 |
| Flexural Strength | 89.0 MPa | 12900 psi | ASTM D790 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
| Compressive Strength | 177 MPa | 25700 psi | ASTM D695 |
| Poissons Ratio | 0.34 | 0.34 | ASTM D638 |
| Shear Modulus | 3.40 GPa | 493 ksi | Calculated |
| Izod Impact, Notched | 0.155 J/cm | 0.290 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.165 J/cm² | 0.785 ft-lb/in² | ASTM D256 |
| Impact | 87 | 87 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.10e+11 ohm-cm | 4.10e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.2 | 5.2 | ASTM D150 |
| Dielectric Strength | 7.70 kV/mm | 196 kV/in | Step by Step; ASTM D149 |
| 11.0 kV/mm | 279 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.059 | 0.059 | ASTM D150 |
| Arc Resistance | 159 sec | 159 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 µm/m-°C @Temperature 40.0 - 130 °C | 27.8 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.490 W/m-K @Temperature 100 °C | 3.40 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 206 °C | 403 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 167 °C | 333 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |
| Oxygen Index | 29.4 % | 29.4 % | ASTM D2863 |
| Shrinkage | 0.288 % | 0.288 % | 72 hr, 120ºC; ASTM D1299 |