- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.078
- 缺口冲击强度: 0.44
- 弯曲强度 [MPa]: 101.0
- 弯曲模量 [MPa]: 15.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.630 g/cc | 0.0228 lb/in³ | ASTM D1895 |
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| Water Absorption | 0.078 % | 0.078 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00090 cm/cm | 0.00090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 94 | 94 | ASTM D785 |
| Tensile Strength, Ultimate | 101 MPa | 14600 psi | ASTM D638 |
| Elongation at Break | 0.84 % | 0.84 % | ASTM D638 |
| Tensile Modulus | 15.3 GPa | 2220 ksi | ASTM D638 |
| Flexural Strength | 163 MPa | 23600 psi | ASTM D790 |
| Flexural Modulus | 15.1 GPa | 2190 ksi | ASTM D790 |
| Compressive Strength | 215 MPa | 31200 psi | ASTM D695 |
| Poissons Ratio | 0.31 | 0.31 | ASTM D638 |
| Shear Modulus | 5.84 GPa | 847 ksi | Calculated |
| Izod Impact, Notched | 0.440 J/cm | 0.824 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ASTM D256 |
| Impact | 206 | 206 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+12 ohm-cm | 2.00e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.0 | 5.0 | ASTM D150 |
| Dielectric Strength | 11.5 kV/mm | 292 kV/in | Step by Step; ASTM D149 |
| 16.3 kV/mm | 414 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.028 | 0.028 | ASTM D150 |
| Arc Resistance | 184 sec | 184 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 49.0 µm/m-°C @Temperature 40.0 - 130 °C | 27.2 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 236 °C | 457 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 279 °C | 534 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 3.10 mm | V-1 @Thickness 0.122 in | |
| Shrinkage | 0.056 % | 0.056 % | 72 hr, 120ºC; ASTM D1299 |