- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.42
- 缺口冲击强度: 0.227
- 弯曲强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 7.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.520 g/cc | 0.0188 lb/in³ | ASTM D1895 |
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.42 % | 0.42 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0058 cm/cm | 0.0058 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 77 | 77 | ASTM D785 |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Tensile Modulus | 6.90 GPa | 1000 ksi | ASTM D638 |
| Flexural Strength | 81.0 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM D790 |
| Compressive Strength | 189 MPa | 27400 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 2.56 GPa | 371 ksi | Calculated |
| Izod Impact, Notched | 0.227 J/cm | 0.425 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.264 J/cm² | 1.26 ft-lb/in² | ASTM D256 |
| Impact | 169 | 169 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.70e+11 ohm-cm | 2.70e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.6 | 6.6 | ASTM D150 |
| Dielectric Strength | 7.90 kV/mm | 201 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.076 | 0.076 | ASTM D150 |
| Arc Resistance | 159 sec | 159 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 44.0 µm/m-°C @Temperature 40.0 - 130 °C | 24.4 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 194 °C | 381 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Shrinkage | 0.43 % | 0.43 % | 72 hr, 120ºC; ASTM D1299 |