- 拉伸强度 [MPa]: 131.0
- 弯曲模量 [MPa]: 17.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 | ||
| Volatiles | 2.0 - 5.0 % @Temperature 163 °C | 2.0 - 5.0 % @Temperature 325 °F | 10 min | ||
| Thickness | 533 microns | 21.0 mil | nominal, cured, per ply | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 70 | 70 | ASTM D2583 | ||
| Tensile Strength, Yield | 131 MPa @Temperature 23.9 °C | 19000 psi @Temperature 75.0 °F | 0° Direction, Dry; 325°F Autoclave; ASTM D638 | ||
| Tensile Modulus | 19.3 GPa @Temperature 23.9 °C | 2800 ksi @Temperature 75.0 °F | 0° Direction, Dry; 325°F Autoclave; ASTM D638 | ||
| Flexural Strength | 200 MPa @Temperature 23.9 °C | 29000 psi @Temperature 75.0 °F | Dry; 325°F Autoclave; ASTM D790 | ||
| Flexural Modulus | 17.9 GPa @Temperature 23.9 °C | 2600 ksi @Temperature 75.0 °F | Dry; 325°F Autoclave; ASTM D790 | ||
| Compressive Strength | 324 MPa @Temperature 23.9 °C | 47000 psi @Temperature 75.0 °F | Dry; 325°F Autoclave; ASTM D695 | ||
| Compressive Modulus | 21.4 GPa @Temperature 23.9 °C | 3100 ksi @Temperature 75.0 °F | Dry; 325°F Autoclave; ASTM D695 | ||
| Shear Strength | 26.9 MPa @Temperature 23.9 °C | 3900 psi @Temperature 75.0 °F | Short Beam; Dry; 325°F Autoclave; ASTM D2344 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.00 J/g-°C | 0.240 BTU/lb-°F | ASTM C351 | ||
| Thermal Conductivity | 4.67 W/m-K @Temperature 149 °C | 32.4 BTU-in/hr-ft²-°F @Temperature 300 °F | ASTM C177 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Filler Content (%) | 2-4 | ||||
| Nominal Prepreg Weight (oz/yd) | 31 | ||||
| Resin Flow (%) | 8-17 | 325°F, 150psi | |||
| Resin Solids Content (%) | 29-35 | ||||