- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 0.1
- 弯曲模量 [MPa]: 28.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.570 g/cc | 0.0206 lb/in³ | ISO 60 | ||
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.10 % | 0.10 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.00020 cm/cm | 0.00020 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 108 MPa | 15700 psi | ISO 527-1 | ||
| Elongation at Break | 0.40 % | 0.40 % | ISO 527-1 | ||
| Tensile Modulus | 31.0 GPa | 4500 ksi | ISO 527-1 | ||
| Flexural Strength | 239 MPa | 34700 psi | ISO 178 | ||
| Flexural Modulus | 28.0 GPa | 4060 ksi | ISO 178 | ||
| Compressive Strength | 200 MPa | 29000 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.09 J/cm² | 5.19 ft-lb/in² | ISO 179-1 | ||
| Charpy Impact, Notched | 0.280 J/cm² | 1.33 ft-lb/in² | ISO 179-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 4.00 µm/m-°C | 2.22 µin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C | 15.0 µin/in-°F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 250 °C | >= 482 °F | ISO 75 Af | ||
| Shrinkage | 0.020 % | 0.020 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||