- 密度 [g/cm3]: 1.58
- 吸水率 [%]: 1.81
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | ISO 60 | ||
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.81 % | 1.81 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0041 cm/cm | 0.0041 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 57.0 MPa | 8270 psi | ISO 527-1 | ||
| Elongation at Break | 0.57 % | 0.57 % | ISO 527-1 | ||
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527-1 | ||
| Flexural Strength | 168 MPa | 24400 psi | ISO 178 | ||
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 | ||
| Compressive Strength | 242 MPa | 35100 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.17 J/cm² | 5.57 ft-lb/in² | ISO 179-1 | ||
| Charpy Impact, Notched | 0.290 J/cm² | 1.38 ft-lb/in² | ISO 179-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 52.0 µm/m-°C | 28.9 µin/in-°F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 213 °C | >= 415 °F | ISO 75 Af | ||
| Shrinkage | 0.11 % | 0.11 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||