- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.2
- 断裂伸长率 [%]: 72.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | ASTM D1895 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Compressive Yield Strength | 221 MPa | 32100 psi | ASTM D695 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.0 | 5.0 | 1MHz; ASTM D150 |
| 7.0 | 7.0 | 60 Hz; ASTM D150 | |
| Dielectric Strength | 15.7 kV/mm | 399 kV/in | ASTM D149 |
| Dissipation Factor | 0.040 | 0.040 | 1 MHz; ASTM D150 |
| 0.090 | 0.090 | 60 Hz; ASTM D150 | |
| Comparative Tracking Index | 180 V | 180 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C @Thickness 1.47 mm | 302 °F @Thickness 0.0579 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.47 mm | 302 °F @Thickness 0.0579 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.47 mm | 302 °F @Thickness 0.0579 in | |
| Flammability, UL94 | V-0 | V-0 | 1.47 mm |
| V-0 | V-0 | 1.47 mm | |