- 密度 [g/cm3]: 1.0733
- 拉伸强度 [MPa]: 7.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.0733 g/cc | 0.038775 lb/in³ | ASTM D3165 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 20 | 20 | ASTM D2240 | ||
| 21 @Treatment Temp. 70.0 °C, Time 252000 sec | 21 @Treatment Temp. 158 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Tensile Strength, Yield | 7.60 MPa | 1100 psi | ASTM D412 | ||
| 4.90 MPa @Treatment Temp. 70.0 °C, Time 252000 sec | 711 psi @Treatment Temp. 158 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Elongation at Break | 705.6 % | 705.6 % | ASTM D412 | ||
| 632.92 % @Treatment Temp. 70.0 °C, Time 252000 sec | 632.92 % @Treatment Temp. 158 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Compressive Modulus | 0.000220 GPa @Strain 5.00 % | 0.0319 ksi @Strain 5.00 % | |||
| 0.000340 GPa @Strain 10.0 % | 0.0493 ksi @Strain 10.0 % | ||||
| 0.000550 GPa @Strain 20.0 % | 0.0798 ksi @Strain 20.0 % | ||||
| 0.000740 GPa @Strain 25.0 % | 0.107 ksi @Strain 25.0 % | ||||
| Compression Set | 6.18 % @Temperature 70.0 °C, Time 79200 sec | 6.18 % @Temperature 158 °F, Time 22.0 hour | ASTM D395 | ||
| Descriptive Properties | |||||
| Color | Black | ||||