- 密度 [g/cm3]: 1.04
- 缺口冲击强度: 2.4
- 弯曲强度 [MPa]: 29.0
- 弯曲模量 [MPa]: 0.980
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0085 cm/cm | 0.0085 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638/D412 |
| Elongation at Break | 80 % | 80 % | ASTM D638/D412 |
| Flexural Modulus | 0.980 GPa | 142 ksi | ASTM D790 |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | ASTM D256 |
| Tear Strength | 120 kN/m | 685 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 110 µm/m-°C @Temperature 20.0 °C | 61.1 µin/in-°F @Temperature 68.0 °F | ASTM D696 |