| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | MSZ ISO 60 | ||
| Particle Size | 600 µm | 600 µm | <1% above | ||
| Viscosity | 2.60e+6 cP @Shear Rate 200 1/s, Temperature 190 °C | 2.60e+6 cP @Shear Rate 200 1/s, Temperature 374 °F | Capillary viscosimeter | ||
| Mooney Viscosity | 85 @Temperature 120 °C | 85 @Temperature 248 °F | ML(1+4); MSZ 11093 ISO 289 | ||
| Crystallinity | <= 1.0 % | <= 1.0 % | Residual; DSC BC HSz 325 | ||
| Collected Volatile Condensable Material | <= 0.30 % | <= 0.30 % | ISO 1269 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 47 | 47 | MSZ ISO 868 | ||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | MSZ ISO 527 | ||
| Elongation at Break | 580 % | 580 % | MSZ ISO 527 | ||
| 100% Modulus | 0.000600 GPa | 0.0870 ksi | MSZ ISO 527 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 3.50 °C | 38.3 °F | DMA method 1 Hz | ||
| Descriptive Properties | |||||
| Chlorine Content, % | 40 | ||||
| Heat Stability at 180°C, minutes | 8 | ||||