- 拉伸强度 [MPa]: 2.8
- 脆化温度 [℃]: -26.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | at 25°C |
| Mooney Viscosity | 48 @Temperature 121 °C | 48 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 70 | 70 | Peak value, at 25°C |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | |
| Tensile Strength, Yield | 2.80 MPa @Strain 100 % | 406 psi @Strain 100 % | |
| Elongation at Break | 320 % | 320 % | |
| Tear Strength | 19.6 kN/m | 112 pli | at 25°C |
| Compression Set | 13 % | 13 % | 70 hours at 25°C |
| 12 % @Temperature 100 °C | 12 % @Temperature 212 °F | 70 hours | |
| 18 % @Temperature 175 °C | 18 % @Temperature 347 °F | 70 hours | |
| 32 % @Temperature 200 °C | 32 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -8.00 °C | 17.6 °F | TR test, TR10 |
| -5.00 °C | 23.0 °F | Gehman torsion test, T10 | |
| -2.00 °C | 28.4 °F | TR test, TR70 | |
| -1.30 °C | 29.7 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -26.0 °C | -14.8 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 3.00 min | 0.0500 hour | Curelastmeter |