- 弯曲强度 [MPa]: 7.79
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.13 g/cc @Temperature 25.0 °C | 1.13 g/cc @Temperature 77.0 °F | |||
| Viscosity | 14000 cP | 14000 cP | dynamic, mixing | ||
| 16000 cP | 16000 cP | dynamic, part B | |||
| 20000 cP | 20000 cP | dynamic, part A | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 32 | 32 | |||
| Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | |||
| Elongation at Break | 500 % | 500 % | |||
| Tear Strength | 29.8 kN/m | 170 pli | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 6.00e+14 ohm-cm | 6.00e+14 ohm-cm | |||
| Dielectric Constant | 2.8 @Frequency 100 Hz | 2.8 @Frequency 100 Hz | |||
| Dielectric Strength | 24.2 kV/mm | 615 kV/in | |||
| Dissipation Factor | 0.0010 @Frequency 100 Hz | 0.0010 @Frequency 100 Hz | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 100 °C | 0.167 hour @Temperature 212 °F | |||
| 50.0 min @Temperature 60.0 °C | 0.833 hour @Temperature 140 °F | ||||
| 1440 min @Temperature 22.0 °C | 24.0 hour @Temperature 71.6 °F | ||||
| Pot Life | 60 min | 60 min | |||
| Shelf Life | 6.00 Month | 6.00 Month | |||
| Descriptive Properties | |||||
| Color | clear | part A | |||
| light grey | part B | ||||
| Hydrophobic | yes | ||||
| Mix Ratio (X:1) | 9 | Base to Catalyst ETN | |||