- 弯曲强度 [MPa]: 16.8
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 | 72 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 16.8 MPa | 2440 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 227 % | 227 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000800 GPa | 0.116 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00540 GPa | 0.783 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 27 % @Temperature 200 °C | 27 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Post Cured 2 hr at 232°C) |