- 密度 [g/cm3]: 1.156
- 弯曲强度 [MPa]: 7.6
- 脆化温度 [℃]: -41.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.156 g/cc | 0.04176 lb/in³ | |
| Mooney Viscosity | 33 @Temperature 100 °C | 33 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 66 | 66 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 7.60 MPa | 1100 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 460 % | 460 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00260 GPa | 0.377 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00470 GPa | 0.682 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00600 GPa | 0.870 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 31.8 kN/m | 181 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 81 % @Temperature 125 °C | 81 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -41.0 °C | -41.8 °F | Temperature Retraction, TR-10 |