- 密度 [g/cm3]: 1.064
- 弯曲强度 [MPa]: 22.0
- 脆化温度 [℃]: -26.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.064 g/cc | 0.03844 lb/in³ | |
| Mooney Viscosity | 48 @Temperature 100 °C | 48 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 78 | 78 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 502 % | 502 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00400 GPa | 0.580 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00840 GPa | 1.22 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.0132 GPa | 1.91 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 43.7 kN/m | 249 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 23 % @Temperature 125 °C | 23 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -26.0 °C | -14.8 °F | Temperature Retraction, TR-10 |