| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | |||
| Mooney Viscosity | 31 @Temperature 121 °C | 31 @Temperature 250 °F | ML1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 75 | 75 | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D2240 | ||
| Tensile Strength at Break | 14.8 MPa | 2150 psi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C | ||
| Elongation at Break | 190 % | 190 % | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C | ||
| 100% Modulus | 0.00603 GPa | 0.875 ksi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C | ||
| Compression Set | 16 % | 16 % | Aged 70 hours @ 200°C, -214 O-rings; ASTM D395 Method B | ||
| Thermal Properties | Metric | English | Comments | ||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 | ||
| Component Elements Properties | Metric | English | Comments | ||
| Fluorine, F | 65.9 % | 65.9 % | |||
| Descriptive Properties | |||||
| Color | Opaque Off-White | ||||
| MH, Maximum Torque | 23.2 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes | |||
| ML, Minimum Torque @ 177°C | 1.1 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes | |||
| Solubility | Ketones and Esters | ||||
| t`50, Time to 50% cure | 2.2 Minutes | 100 cpm, 0.5° Arc, 6 Minutes | |||
| t`90 - Time to 90% cure | 3.1 Minutes | 100 cpm, 0.5° Arc, 6 Minutes | |||
| ts2 - Time to 2 in-lb rise from min | 1.8 Minutes | 100 cpm, 0.5° Arc, 6 Minutes | |||