- 密度 [g/cm3]: 1.19
- 弯曲强度 [MPa]: 15.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | B Component; ASTM D1475 |
| 1.23 g/cc | 0.0444 lb/in³ | A Component; ASTM D1475 | |
| Viscosity | 30000 cP | 30000 cP | A Component; ASTM D1824 |
| 45000 cP | 45000 cP | B Component; ASTM D1824 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 80 | 80 | Cured property; ASTM D2240 |
| Tensile Strength, Ultimate | 15.2 MPa | 2200 psi | Cured property; ASTM D638 |
| Elongation at Break | 200 % | 200 % | Cured property; ASTM D638 |
| Adhesive Bond Strength | 13.8 MPa | 2000 psi | Al-to-Al Lap Shear; Cured property; ASTM D1002; 50 grit, sanded/solvent wiped |
| Thermal Properties | Metric | English | Comments |
| Flash Point | >= 125 °C | >= 257 °F | A Component; ASTM D92 |
| >= 125 °C | >= 257 °F | B Component; ASTM D92 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 65.0 °C | 149 °F | Cure 2 hrs; with RT gel |