- 密度 [g/cm3]: 1.09
- 断裂伸长率 [%]: 76.0
- 弯曲强度 [MPa]: 48.0
- 弯曲模量 [MPa]: 2.03
- 热变形温度 [℃]: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 | 75 | ASTM D2240 |
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638/D412 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638/D412 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | at 5% strain; ASTM D790 |
| Flexural Modulus | 2.03 GPa | 294 ksi | ASTM D790 |
| Izod Impact, Unnotched | 4.30 J/cm | 8.06 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.20e+14 ohm-cm | 5.20e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 7.90e+14 ohm | 7.90e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.07 @Frequency 1e+6 Hz | 3.07 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 101 µm/m-°C @Temperature 20.0 °C | 56.1 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| UL RTI, Electrical | 90.0 °C @Thickness 3.20 mm | 194 °F @Thickness 0.126 in | UL746B |
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 3.20 mm | 176 °F @Thickness 0.126 in | UL746B |
| UL RTI, Mechanical without Impact | 90.0 °C @Thickness 3.20 mm | 194 °F @Thickness 0.126 in | UL746B |
| Flammability, UL94 | 5VA | 5VA | UL94 |
| V-0 @Thickness 3.18 mm | V-0 @Thickness 0.125 in | UL94 | |