| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792-66 | ||
| Brookfield Viscosity | 176 cP | 176 cP | Part A; ASTM D2393 | ||
| 300 cP | 300 cP | Mixed | |||
| 450 cP | 450 cP | Part B | |||
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ASTM D2566 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 72 - 78 | 72 - 78 | ASTM D2240-68 | ||
| Elongation at Break | 11.2 % | 11.2 % | ASTM D638 | ||
| Flexural Modulus | 2.042 GPa | 296.2 ksi | |||
| Thermal Properties | Metric | English | Comments | ||
| Heat Distortion Temperature | 62.8 °C | 145 °F | 24 Hours at 75°F | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 - 60.0 min @Temperature 25.0 °C | 0.500 - 1.00 hour @Temperature 77.0 °F | demold time | ||
| Pot Life | 3.0 min @Temperature 24.0 °C | 3.0 min @Temperature 75.2 °F | gel time, 200g; ASTM 2471-71 | ||
| Descriptive Properties | |||||
| Mix Ratio | 1:1 by weight or volume | ||||