- 弯曲强度 [MPa]: 41.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792-66 | ||
| Brookfield Viscosity | 200 - 400 cP @Temperature 23.9 °C | 200 - 400 cP @Temperature 75.0 °F | Mixed; ASTM D2393 | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 79 | 79 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 41.2 MPa | 5980 psi | ASTM D638 | ||
| Elongation at Break | 6.4 % | 6.4 % | ASTM D638-72 | ||
| Flexural Strength | 60.7 MPa | 8810 psi | ASTM D790 | ||
| Compressive Strength | 44.5 MPa | 6460 psi | ASTM D695 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat Distortion Temperature | 58.3 °C | 137 °F | 24 Hours at 75°F | ||
| 62.8 °C | 145 °F | 7 Days at 75°F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 7.00 - 10.0 min @Temperature 25.0 °C | 0.117 - 0.167 hour @Temperature 77.0 °F | demold time | ||
| Pot Life | 0.750 min @Temperature 24.0 °C | 0.750 min @Temperature 75.2 °F | Gel time, 4 oz. mass; ASTM D2471-71 | ||
| Descriptive Properties | |||||
| Mix Ratio | 100:88 by weight, 100:100 by volume, resin/harder | ||||