- 密度 [g/cm3]: 2.29
- 吸水率 [%]: 0.11
- 弯曲强度 [MPa]: 6.89
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.29 g/cc | 0.0827 lb/in³ | Cured | ||
| Water Absorption | 0.11 % | 0.11 % | 24 hours | ||
| Water Absorption at Saturation | 0.0028 % | 0.0028 % | 30 Days | ||
| Viscosity | 18800 cP @Temperature 25.0 °C | 18800 cP @Temperature 77.0 °F | |||
| Linear Mold Shrinkage | 0.0098 cm/cm | 0.0098 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 62 - 70 | 62 - 70 | |||
| Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |||
| Elongation at Break | 35 % | 35 % | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 1.20e+15 ohm-cm | <= 1.20e+15 ohm-cm | |||
| Surface Resistance | 1.80e+14 ohm | 1.80e+14 ohm | |||
| Dielectric Constant | 5.9 @Frequency 1000 Hz | 5.9 @Frequency 1000 Hz | |||
| Dielectric Strength | 21.7 kV/mm @Thickness 1.59 mm | 550 kV/in @Thickness 0.0625 in | |||
| Dissipation Factor | 0.045 @Frequency 1000 Hz | 0.045 @Frequency 1000 Hz | |||
| Arc Resistance | >= 120 sec | >= 120 sec | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 120 µm/m-°C @Temperature 20.0 °C | 66.7 µin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 0.586 W/m-K | 4.06 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 130 °C | 266 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 min | 4.00 hour | 100°C | ||
| 360 min | 6.00 hour | 60°C | |||
| 10080 min | 168.0 hour | 25°C | |||
| Pot Life | 25 - 30 min | 25 - 30 min | Value for 1 lbm at 25°C | ||
| Descriptive Properties | |||||
| Color | Light Tan | ||||